Synthesis, structural and electrical properties of triethylene glycol (TREG) stabilized Mn0.2Co0.8Fe2O4 NPs

Deligoz H., Baykal A., Tanriverdi E. E., Durmus Z., Toprak M. S.

MATERIALS RESEARCH BULLETIN, cilt.47, sa.3, ss.537-543, 2012 (SCI-Expanded, Scopus)

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 47 Sayı: 3
  • Basım Tarihi: 2012
  • Doi Numarası: 10.1016/j.materresbull.2011.12.050
  • Dergi Adı: MATERIALS RESEARCH BULLETIN
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.537-543
  • Anahtar Kelimeler: Magnetic materials, Chemical synthesis, Impedance spectroscopy, Dielectric properties, Magnetic properties, MAGNETIC-PROPERTIES, COBALT FERRITE, THIN-FILMS, MAGNETOSTRICTIVE PROPERTIES, DIELECTRIC-PROPERTIES, CURIE-TEMPERATURE, IRON-OXIDE, NANOPARTICLES, CONDUCTIVITY, RELAXATION
  • İstanbul Üniversitesi-Cerrahpaşa Adresli: Hayır

Özet

Triethylene glycol (TREG) stabilized Mn0.2Co0.8Fe2O4 NPs was synthesized by a glycothermal reaction. XRD analysis identified the product as Mn0.2Co0.8Fe2O4 with a high phase purity. Nano-sized particles with an average size of about 6-8 nm were obtained with nearly single crystalline nature with TEM analysis. Superparamagnetic-like behavior of TREG stabilized Mn0.2Co0.8Fe2O4 NPs was observed by VSM. The binding between TREG and Mn0.2Co0.8Fe2O4 NPs was investigated with FT-IR and found to be via O on the TREG and NP surface. TG analysis indicated that the Mn0.2Co0.8Fe2O4 NP content was about 40%, with a TREG-shell content to be around 60%. Overall conductivity of the nanocomposite is in the range of 10(-10) to 10(-7) S cm(-1) with a strong dependence on temperature and frequency, indicating ionic conductivity. The nanocomposite exhibited lower epsilon' and epsilon '' compared to TREG stabilized Mn0.2Co0.8Fe2O4 NPs due to the doping of co-doping of manganese and cobalt. (C) 2012 Elsevier Ltd. All rights reserved.

Triethylene glycol (TREG) stabilized Mn0.2Co0.8Fe2O4 NPs was synthesized by a glycothermal reaction. XRD analysis identified the product as Mn0.2Co0.8Fe2O4 with a high phase purity. Nano-sized particles with an average size of about 6–8 nm were obtained with nearly single crystalline nature with TEM analysis. Superparamagnetic-like behavior of TREG stabilized Mn0.2Co0.8Fe2O4 NPs was observed by VSM. The binding between TREG and Mn0.2Co0.8Fe2O4 NPs was investigated with FT-IR and found to be via O on the TREG and NP surface. TG analysis indicated that the Mn0.2Co0.8Fe2O4 NP content was about 40%, with a TREG-shell content to be around 60%. Overall conductivity of the nanocomposite is in the range of 10−10 to 10−7 S cm−1 with a strong dependence on temperature and frequency, indicating ionic conductivity. The nanocomposite exhibited lower ?’ and ?″ compared to TREG stabilized Mn0.2Co0.8Fe2O4 NPs due to the doping of co-doping of manganese and cobalt.