Flat-pressed Wood Plastic Composite as an Alternative to Conventional Wood-based Panels

Ayrilmis N., JARUSOMBUTI S.

JOURNAL OF COMPOSITE MATERIALS, cilt.45, sa.1, ss.103-112, 2011 (SCI-Expanded, Scopus) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 45 Sayı: 1
  • Basım Tarihi: 2011
  • Doi Numarası: 10.1177/0021998310371546
  • Dergi Adı: JOURNAL OF COMPOSITE MATERIALS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.103-112
  • Anahtar Kelimeler: hot press molding, polypropylene, reinforced thermoplastic, rubberwood, water resistance, wood plastic composite
  • İstanbul Üniversitesi-Cerrahpaşa Adresli: Evet

Özet

This study evaluated physical and mechanical properties of the wood plastic composite panels made from dry-blended rubberwood fiber-polypropylene (PP) powder formulations using a conventional flat-press process under laboratory conditions. Three levels of rubberwood fibers (Hevea brasiliensis), 40%, 50%, and 60% based on the composition by weight, were mixed with the PP powder without and with 3% (based on weight) maleic anhydride grafted PP (MAPP) as a coupling agent. Water resistance of the panels was negatively influenced by the increasing wood fiber content. The modulus of rupture of the panels significantly increased with the increase in the wood fiber content from 40 to 50wt% and then decreased as the fiber content reached 60wt% but this decrease was not significant. The modulus of elasticity of the panels increased with the increase in fiber content from 40 to 60wt%. Internal bond strength and screw withdrawal resistance declined with the increase in fiber content from 40% to 60wt%. The formulations with MAPP were found to have higher strength and better water resistance.