Synthesis of four-component acrylic-modified water-reducible alkyd resin: investigation of dilution ratio effect on film properties and thermal behaviors

Buyukyonga O. N., Akgun N., Acar I., Guclu G.

JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, cilt.14, sa.1, ss.117-128, 2017 (SCI-Expanded, Scopus) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 14 Sayı: 1
  • Basım Tarihi: 2017
  • Doi Numarası: 10.1007/s11998-016-9835-z
  • Dergi Adı: JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.117-128
  • Anahtar Kelimeler: Water-reducible alkyd resin, Acrylic modification, Film properties, Dilution ratio effect, VOLATILE ORGANIC-COMPOUNDS, INDOOR ENVIRONMENTS, WASTE PET, COATINGS, OIL, AMINOGLYCOLYSIS, EXPOSURE, EMULSION, BINDERS
  • İstanbul Üniversitesi-Cerrahpaşa Adresli: Hayır

Özet

This study investigated the effect of the dilution ratio on film properties of acrylic-modified water-reducible alkyd resins. First, new four-component acrylic-modified alkyd resins based on 1,3-propanediol containing 40% of the equivalent amount of acrylic copolymer to alkyd resin were synthesized using the fatty acid method. The synthesized acrylic-modified alkyd resin was then dissolved in isopropyl alcohol (IPA) at various ratios and further diluted using distilled water at various ratios to obtain by-weight percentages of 70/50, 70/60, and 80/60 of solid content to IPA and water, respectively. Films of the modified alkyd resins were prepared, and cured at 150A degrees C for 1 h, then their physical and chemical surface coating properties and thermal behaviors were investigated. The best results were obtained for the by-weight percentages of 80/60.