Investigation of the Usage of Depolymerized Nylon 66 Intermediate in Phenolic Resin Modification

EMİK S., Yilmaz B. Y., Lyim T. B.

POLYMER-PLASTICS TECHNOLOGY AND MATERIALS, cilt.58, sa.4, ss.454-463, 2019 (SCI-Expanded, Scopus) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 58 Sayı: 4
  • Basım Tarihi: 2019
  • Doi Numarası: 10.1080/03602559.2018.1482920
  • Dergi Adı: POLYMER-PLASTICS TECHNOLOGY AND MATERIALS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.454-463
  • Anahtar Kelimeler: Depolymerization, hydrolysis of Nylon 66, novolac, Nylon 66, recycling, THERMAL-STABILITY, DECOMPOSITION BEHAVIOR, FORMALDEHYDE RESIN, COMPOSITES, SILICON, POLYBENZOXAZINE, SPECTROSCOPY, DEGRADATION, RESISTANCE, NMR
  • İstanbul Üniversitesi-Cerrahpaşa Adresli: Evet

Özet

In this study, the potential usage of the Nylon 66 hydrolysis products (HP) for curing "high ortho" novolac resin (N) was investigated. According to FTIR, DSC and TGA results, it is concluded that HP can be as a curing agent for N without the need for another crosslinking agent and thermal degradation stability of cured N-HP blends increased significantly up to 15% HP content. Furthermore, according to performed surface coating tests, it is shown that all films prepared with HP up to 30-wt % have excellent water resistance, drying and adhesion properties as well as with high hardness values.